| Study on Oxygen Delignification of Pinus Massoniana Prehydrolysis Sulfate Pulp |
| |
| DOI：10.11980/j.issn.0254-508X.2011.12.001 |
| Key Words:pinus massoniana prehydrolysis sulfate pulp oxyen delignification prehydrolysis infrared spectrum |
| Author Name | Affiliation | | 屈琴琴1 | 1.长沙理工大学化学与生物工程学院,湖南长沙,410114 | | 马乐凡1 | 1.长沙理工大学化学与生物工程学院,湖南长沙,410114 | | 周鲲鹏2 | 2.湖南骏泰浆纸有限责任公司,湖南怀化,418005 | | 潘晓锋1 | 1.长沙理工大学化学与生物工程学院,湖南长沙,410114 | | 谭丽红1 | 1.长沙理工大学化学与生物工程学院,湖南长沙,410114 | | 曾 凯1 | 1.长沙理工大学化学与生物工程学院,湖南长沙,410114 |
|
| Hits: 8694 |
| Download times: 2741 |
| Abstract:In this paper, the oxyen delignification process of pinus massoniana prehydrolysis sulfate pulp was studied, the mechanism of oxyen delignification of prehydrolysis sulfate pulp was discussed based on the comparison of oxyen delignification of prehydrolysis sulfate pulps at different prehydrolysis degree with oxyen delignification of KP pulp. The optimal conditions of oxygen delignification of pinus massoniana prehydrolysis sulfate pulp was found that the dosage of alkali 3%, temperature 100℃,reaction time 60 min, oxygen pressure between 0.5 MPa and 0.6 MPa, MgSO4 charge 0.2%.The oxyen delignification rate of prehydrolysis sulfate pulp was higher than that of KP pulp,and increased linearly with reaction time of prehydrolysis,but viscosity reduction rate was lower than that of KP plup. The infrared spectra analysis indicated that the removal of guaiacyl during oxyen delignification of prehydrolysis sulfate pulp was more than that of KP pulp,and relative intensity decrease of carbohydrate absorption peaks during oxyen delignification of prehydrolysis sulfate pulp was less than that of KP pulp. |
| View Full Text HTML View/Add Comment Download reader |
|
|
|