Effect of Silane Modified Cellulosic Micro-nano Particles on Super-hydrophobicity of Material
  
DOI:10.11980/j.issn.0254-508X.2018.12.003
Key Words:nanocellulose  superhydrophobic  micro-nano particle  silanization  fluoroalkyl silane
Fund Project:国家自然科学基金(31570569);广州市科技计划(201704020038);制浆造纸工程国家重点实验室基金(2017QN01)。
Author NameAffiliation
ZHU Zhao-dong1 1.State Key Lab of Pulp and Paper Engineering South China University of Technology Guangzhou Guangdong Provence 510640 
ZHENG Xue-mei1 1.State Key Lab of Pulp and Paper Engineering South China University of Technology Guangzhou Guangdong Provence 510640 
FU Shi-yu1,* 1.State Key Lab of Pulp and Paper Engineering South China University of Technology Guangzhou Guangdong Provence 510640 
ZHU Wen-yuan2 2.Jiangsu Provincial Key Lab of Pulp and Paper Science and Technology Nanjing Forestry University Nanjing Jiangsu Provence 210037 
Hits: 8859
Download times: 3010
Abstract:The feature of superhydrophobic material surface is micro-nano structure coated with low surface energy substance.The prepared CNC was spray-dried to obtain micro-nanoparticles(CNCmp), which was modified by chemical vapor deposition using MTMS.The modified CNCmps were used to prepare superhydrophobic coatings, and sprayed on the filter paper to form super-hydrophobic-filter-paper.The silanization reaction was critical for superhydrophobic coatings preparation.It was found that the amount of MTMS used in the silanization reaction in a designed device was optimized as 70 μL, the reaction temperature was 25℃, and the reaction time was 10 min. Silane modified micro-nanocellulose particles could be used to prepare superhydrophobic coatings.It was also found that there was no difference for the superhydrophobic materials prepared by modification using fluorosilane PFOTES and MTMS.