| Application of Nano Cellulose in Tobacco Sheet Prepared by Papermaking Process |
| |
| DOI：10.11980/j.issn.0254-508X.2018.01.003 |
| Key Words:nano cellulose tobacco sheet papermaking process physical property |
| Fund Project:高浓/高剪切工况微纤化纤维素阳离子改性反应特性(16JCZDJC37700)；云南中烟再造烟叶科技项目(XM-J201602)。 |
| Author Name | Affiliation | | 刘雄利1 | 1.天津科技大学天津市制浆造纸重点实验室,天津,300457 | | 张 昊1 | 1.天津科技大学天津市制浆造纸重点实验室,天津,300457 | | 陈岭峰2 | 2.云南中烟再造烟叶有限责任公司,云南昆明,650106 | | 郭 辉2 | 2.云南中烟再造烟叶有限责任公司,云南昆明,650106 | | 武士杰2，* | 2.云南中烟再造烟叶有限责任公司,云南昆明,650106 | | 刘 忠1 | 1.天津科技大学天津市制浆造纸重点实验室,天津,300457 | | 刘洪斌1 | 1.天津科技大学天津市制浆造纸重点实验室,天津,300457 | | 温洋兵1，* | 1.天津科技大学天津市制浆造纸重点实验室,天津,300457 |
|
| Hits: 5650 |
| Download times: 1972 |
| Abstract:The application of nano cellulose in tobacco sheet prepared by papermaking processes was studied in order to improve the physical property of tobacco sheet therefore reduce wood pulp fibers usage.The results showed that the surface cationization of nanofibrillated cellulose(NFC） could effectively improve the tensile index of tobacco sheet. When the addition of NFC with surface cationization was 0.1% on dried tobacco slurry and wood pulp content was 16.7%， the tensile index and bulk were 10.69 N·m/g and 1.99 cm3/g respectively comparing tensile index and bulk were 10.87 N·m/g and 2.04 cm3/g respectively for the control sample with wood pulp content 25% and withoutthe addition of NFC． |
| View Full Text HTML View/Add Comment Download reader |
|
|
|