| Study on Preparation of Lignin-containing Cellulose Nanofibril with Acidic Deep Eutectic Solvents and Its Composite Film |
| Received:August 07, 2022 |
| DOI：DOI：10.11980/j.issn.0254-508X.2023.03.006 |
| Key Words:deep eutectic solvent pretreatment lignin-containing cellulose nanofibril polyvinyl alcohol |
| Fund Project:国家自然科学基金项目（32071715）。 |
| Author Name | Affiliation | Postcode | | LI Zhan* | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 | | JIANG Chuang | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 | | NING Chenxi | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 | | REN Qian | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 | | HOU Qingxi | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 | | LIU Wei | School of Light Industry Science and Engineering, Tianjin University of Science & Technology, Tianjin, 300457
State Key Lab of Biobased Fiber Manufacturing Technology, Tianjin University of Science & Technology, Tianjin, 300457 | 300457 |
|
| Hits: 5754 |
| Download times: 3566 |
| Abstract:Lignin-containing cellulose nanofibril （LCNF） was prepared by acidic deep eutectic solvent （DES） pretreatment combined with high pressure homogenization， and was co-blended with polyvinyl alcohol （PVA） to form LCNF/PVA composite film. The effects of two acidic DES pretreatments were investigated， the properties of LCNF were compared and analyzed， the performance of the LCNF/PVA composite film was discussed. The results showed that the extractions of hemicellulose by lactic acid-choline chloride （LC） and acetic acid-choline chloride （AC） both were more than 78%， and the lignin extraction was as high as 61.2% after LC pretreatment with ethanol washing. After DES pretreatment， ethanol washing was beneficial to separation of lignin. The diameter of cellulose nanofilament prepared by LC （LC-E-LCNF） was 50~100 nm. Compared with pure PVA film， the hydrophobicity of LCNF/PVA composite film was significantly improved， and its stress was raised to 70.3 MPa， and its UV blocking ability was approximately 100%. It had good thermal stability and haze， as well as certain freshness preservation performance， which was expected to be used in the food packaging field. |