Fabrication and Analysis of Electric Heating Property of Carbon Black/Aramid Fibrid/ Carbon Fiber-based Paper
Received:January 13, 2022  
DOI：10.11980/j.issn.0254-508X.2022.09.001
Key Words:carbon fiber-based paper  electric heating  wet-forming process
Fund Project:陕西省重点研发计划项目（2021ZDLGY14-05）；国家自然科学基金项目（22178211）；西安市科技计划项目（2019220114SYS016CG038）；陕西省教育厅重点项目（20JY002）；浙江省重点研发计划项目（2019C04008）。
Author NameAffiliationPostcode
GUO Zizhan* Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
JIA Fengfeng Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
DONG Jiayue Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
LIU Yuanqing Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
WANG Haoran Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
DAI Xiyi Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
LU Zhaoqing Shaanxi Province Key Lab of Papermaking Technology and Specialty Paper， College of Bioresources Chemical and Materials Engineering， Shaanxi University of Science & Technology， Xi’an， Shaanxi Province， 710021 710021
Hits: 2389
Download times: 1741
Abstract:Using carbon fiber as electric heating skeleton， carbon black as conductive path， and aramid fibrid as auxiliary forming slurry， the carbon black/aramid fibrid/carbon fiber-based paper was fabricated via wet-forming process. The results showed that the paper comprising of 10% carbon black， 20% aramid fibrid， and 70% carbon fiber after impregnated with 15% phenolic resin and hot-press exhibited the best comprehensive performance. The tensile strength， tearing strength， and sheet resistance of the paper reached 1989 kN/m， 1057 mN， and 1.5 Ω/□， respectively. With supplied voltage of 8 V， the highest surface temperature of the paper after electric heating could reach 242.5℃.