Preparation of Cellulose Nanofibril by Alkaline Oxidation Process with NaClO2 |
Received:December 12, 2019 |
DOI:10.11980/j.issn.0254-508X.2020.03.005 |
Key Words:NaClO2 oxidation high-pressure homogenization cellulose nanofibril zeta potential |
Author Name | Affiliation | Postcode | WANG Dongsheng | Tianjin Key Lab of Pulp and Paper, Tianjin University of Science & Technology,Tianjin,300457 | 300457 | YANG Qiulin | Tianjin Key Lab of Pulp and Paper, Tianjin University of Science & Technology,Tianjin,300457 Shandong Huatai Paper Co., Ltd.,Dongying,Shandong Province,257335 | 257335 | LIU Qiujuan | Tianjin Key Lab of Pulp and Paper, Tianjin University of Science & Technology,Tianjin,300457 | 300457 |
|
Hits: 4970 |
Download times: 3330 |
Abstract:In the present work, a combined method involving oxidation and high-pressure homogenization was used to treat the autohydrolyzed BKP (bleached softwood kraft pulp) for preparing cellulose nanofibril(CNF). Under alkaline condition, NaClO2 was used as an oxidant to decrease the zeta potential and the DP of the pulp. The oxidation time, temperature, NaClO2 dosage, as well as the pulp consistency were optimized, the zeta potential of the oxidized pulp, and the consumption of NaClO2 were determined. The results showed that the zeta potential of the oxidized pulp was obviously decreased, and the optimum conditions of oxidation were as follows: pulp consistency 10%, NaClO2 dosage 8%, oxidation time 6 h, and oxidation temperature 95℃. Under that optimized conditions, the zeta potential of the oxidized pulp was -37.6 mV, with a decrease of 43% compairing to the autohydorlyzed pulp. The oxidized pulp was treated using high-pressure homogenization to obtain CNF, and the dimension, viscosity, TG as well as the zeta potential of the CNF were analyzed. The results showed that the CNF with a good size distribution was prepared when the oxidized pulp was homogenized under 80 MPa for 70 times. The diameter distribution of the CNF was mainly in the range of 20~60 nm, and its length-to-diameter ratio was over 100. The zeta potential of the CNF was as low as -42.3 mV, indicating that the CNF had a good dispersion stability in aqueous medium. |
View Full Text HTML View/Add Comment Download reader |
|
|
|