![本文二维码信息](/download_upload_file.aspx?file_name=/uploadfile/two_dimensional_code_img/zgzzen/2017/2/201702001.png) 二维码(扫一下试试看!) |
Improvement of APMP Pulp Properties by Using Cinnamoylated Xylans as Additive |
|
DOI:10.11980/j.issn.0254-508X.2017.02.001 |
Key Words:cinnamoylated xylans xylan derivative APMP pulp properties |
Fund Project:本课题得到国家自然科学基金(31370580,31470602)、山东省重大科技专项(2014ZZCX09101,2015ZDZX09002)和泰山学者工程专项经费的资助。 |
Author Name | Affiliation | 周慧芳 | 齐鲁工业大学制浆造纸科学与技术教育部重点实验室,山东济南,250353 | 杨桂花* | 齐鲁工业大学制浆造纸科学与技术教育部重点实验室,山东济南,250353 | 陈嘉川* | 齐鲁工业大学制浆造纸科学与技术教育部重点实验室,山东济南,250353 | 孔凡功 | 齐鲁工业大学制浆造纸科学与技术教育部重点实验室,山东济南,250353 | 王 强 | 齐鲁工业大学制浆造纸科学与技术教育部重点实验室,山东济南,250353 |
|
Hits: 6386 |
Download times: 1813 |
Abstract:In this study improvement of the properties of alkaline peroxide mechanical pulp (APMP) by using cinnamoylated xylans (CX) with different degrees of substitution (DS) were investigated. The results showed that the physical strength properties of APMP were significangtly improved by using CX as additive. The optimal DS of CX was 0.18, and the optimal application conditions of adding CX were 15 min of mixing time and 1.0% of CX dosage, in which the physical strength properties and papermaking performance of APMP were optimal. Compared with the control APMP without additive, the breaking length, burst index, tear index, and brightness of the added APMP increased by 37.4%, 90.5%, 19.0% and 3.7% respectively. When blending KP and APMP to prepare the furnish, adding CX could obtain the similar strength of the paper by reducing the proportion of KP or increasing the proportion of APMP. The analysis of SEM and FT-IR spectra indicated that CX was adsorbed on the surface of the pulp fibers, which decreased the porosity between the fibers and improved the uniformity of paper surface. |