| Effect of Modified Nano- Al2O3 on Properties of Aramid Paper |
| |
| DOI：10.11980/j.issn.0254-508X.2016.04.008 |
| Key Words:aramid paper silicon coupling agent nano- Al2O3 performance |
| Fund Project:陕西省2015科技统筹创新工程计划，项目编号2015KTCQO1-44；国家863项目子课题名称“粉煤灰提取氧化硅生产高填料文化用纸技术（2011AA06A101）”。 |
| Author Name | Affiliation | | 张素风 | 陕西科技大学轻工与能源学院,陕西省造纸技术及特种纸品开发重点实验室,陕西西安，710021 | | 张美娟 | 陕西科技大学轻工与能源学院,陕西省造纸技术及特种纸品开发重点实验室,陕西西安，710021 | | 豆莞莞 | 陕西科技大学轻工与能源学院,陕西省造纸技术及特种纸品开发重点实验室,陕西西安，710021 | | 蒋莹莹 | 陕西科技大学轻工与能源学院,陕西省造纸技术及特种纸品开发重点实验室,陕西西安，710021 | | 李鹏辉 | 陕西科技大学轻工与能源学院,陕西省造纸技术及特种纸品开发重点实验室,陕西西安，710021 |
|
| Hits: 5249 |
| Download times: 1438 |
| Abstract:Nano- Al2O3 particles were modified with four different amount of silicon coupling agent KH-550 and the modified nano- Al2O3 particle size was measured. At the same time, the effects of addition amount of modified nano- Al2O3 on tensile strength, dielectric strength, tightness properties of aramid paper were studied. The tensile strength and dielectric strength of the aramid paper before and after adding nano- Al2O3 were compared. The results showed that the nano- Al2O3 particle size was reduced after modification. When the ratio of nano- Al2O3 and silicon coupling agent KH-550 was 5 g∶15 mL, the amount of modified nano- Al2O3 was 6%, the tensile strength of the paper increased by 58.3%, the dielectric strength increased by 37.0%, the paper tightness did not change significantly. |
| View Full Text HTML View/Add Comment Download reader |
|
|
|