| 棉浆纤维磷酸酯化及其对打浆性能的影响 |
| Effect of Phosphate Esterification of Cotton Pulp on Its Beating Performance |
| 收稿日期： |
| DOI：10.11980/j.issn.0254-508X.2017.09.003 |
| 关键词: 棉浆纤维 纤维素磷酸酯 酯化剂 微观结构 |
| Key Words:cotton fiber cellulose phosphate esterification agent microstructure |
| 基金项目:国家自然科学基金项目（31370578）。 |
|
| 摘要点击次数: 5533 |
| 全文下载次数: 1735 |
| 摘要:以棉浆纤维为原料，混合磷酸盐Na2HPO4-NaH2PO4为酯化剂，制备纤维素磷酸酯，研究酯化剂用量、反应温度、时间、pH值等对纤维润胀性能和取代度的影响。结果表明，制备纤维素磷酸酯的最佳条件为：酯化剂用量12%，反应温度120℃，反应时间1.5 h，pH值6.0、酯化剂配比1∶1，尿素用量4%，在此条件下，所制备的纤维素磷酸酯取代度为0.032，保水值从92.86%提高到134.12%；经磷酸酯化改性后的棉纤维表面发生了明显的局部塌陷与扭曲，破坏了束缚纤维细胞壁S2层的初生壁及次生壁外层S1，显著改善了棉纤维的打浆性能。 |
| Abstract:Phosphate esterification of cotton pulp was carried out using Na2HPO4/NaH2PO4 as esterification agent. The optimum technology of cellulose phosphate esterification with half wet process was investigated by orthogonal experiments, and the DS of the product was analyzed by spectrophotometry. The optimum condition of cellulose phosphate esterification were as follows: the dosage of esterification agent 12%, reaction temperature 120℃, reaction time 1.5 h, pH 6.0, Na2HPO4/NaH2PO4 ratio 1∶1, dosage of urea 4%. Under this condition, the degree of substitution of cellulose phosphate was 0.032, the water retention value of the pulp increased from 92.86% to 134.12%; the surface of the cotton fiber after phosphate esterification had obvious local collapse and distortion, which were caused by the damage of the primary wall and outer layer of secondary wall of the fiber, which significantly improved the beating performance of cotton pulp． |
| 查看全文 HTML 查看/发表评论 下载PDF阅读器 |