| 木质素磺酸钠接枝共聚物的制备与抑尘性能研究 |
| Preparation of Lignosulfonate Sodium and Sodium Acrylate Graft Copolymer and Its Dust Suppressant Performance |
| 收稿日期： |
| DOI：10.11980/j.issn.0254-508X.2019.06.007 |
| 关键词: 木质素磺酸钠 接枝共聚 丙烯酸钠 抗风蚀性能 抑尘性能 |
| Key Words:lignosulfonate sodium graft copolymer sodium acrylate anti-wind erosin performance dust suppression performance |
| 基金项目:国家自然科学基金(31700515)；天津市级大学生创新创业训练计划项目(201810057157)。 |
|
| 摘要点击次数: 6940 |
| 全文下载次数: 1995 |
| 摘要:采用正交实验法优化木质素磺酸钠(Ls-Na)接枝丙烯酸钠(SAA)抑尘剂的制备工艺，利用傅里叶变换红外光谱仪、扫描电子显微镜和热重分析仪对接枝共聚物(Ls-Na-SAA)进行表征，并考察了木质素磺酸钠接枝前后作为抑尘剂的性能差异。结果表明，木质素磺酸钠与丙烯酸钠成功接枝，接枝后共聚物热稳定性提高。木质素磺酸钠接枝的最优条件为：反应温度65℃、反应时间3 h、中和度60%、引发剂过硫酸钾质量分数10%。与Ls-Na相比，Ls-Na-SAA的保水性基本不变；喷洒质量分数2.5%Ls-Na-SAA时，沙样的抗压能力由37.0 kPa提高到455.6 kPa，喷洒质量分数1.5%Ls-Na-SAA时，沙样的质量损失率由25.2%降低到3.1%。接枝共聚后Ls-Na-SAA形成网状交联结构，在沙粒之间形成更多的黏结物，进而提高其抗压性及抗风蚀性能。 |
| Abstract:An orthogonal design was applied to optimize lignosulfonate sodium(Ls-Na) grafting copolymerization with sodium acrylate(SAA). The lignosulfonate graft copolymer(Ls-Na-SAA) was characterized by FT-IR， SEM and TGA. The results showed that sodium acrylate was grafted onto the lignosulfonate sodium successfully and the graft copolymer exhibited enhanced thermal stability. Under the optimized grafting conditions(temperature 65℃， reaction time 3 h， neutralization degree 60% and initiator concentration 10%)， the performances of Ls-Na and Ls-Na-SAA as dust suppressants were analyzed and compared. The results indicated that the water retention capacity of Ls-Na-SAA was basically unchanged after the grafting， its compression strength increased from 37.0 kPa to 455.6 kPa when the mass fraction of spraying was 2.5% and the sand loss rate decreased from 25.2% to 3.1% when the mass fraction of spraying was 1.5%. After grafting copolymerization， Ls-Na-SAA formed a reticular cross linking structure and more binding layers among the sand particles. These features contributed to the improved compressive strength and anti-wind erosion performance of Ls-Na-SAA. |